Following on from last week's article I'm going to talk about armour once again, this time Krupp Steel! Now this has probably been discussed on just about any forum you care to name at such great lengths before that you're already likely familiar with the argument.
If you're not, it's that German steel was somehow superior, however, as the war went on lack of resources meant that German armour quality deteriorated. There are some comments from the renowned German armour historians Jentz and Doyle that are used to parry the blows of the Allies, as they seem to say the opposite of the reports cited by the deteriorating war situation crowd.
Now while talking about this on a forum I frequent, I was reminded of a document I'd seen previously, and have mentioned on here, about the quality of Japanese armour. That's the point at which I formed a new theory, that might account for the disagreements around this subject.

The issue here is that pretty much everyone you speak to on the subject has an axe to grind. It's either fervent wehraboos complaining Germany would have won if it wasn't for those pesky bombers. On the other side you have what seems to be mostly Soviet (but I'm sure we can find some British or American fanboys wading in) fanatics ranting about how they're superior when it comes to designing armour. So as each side has an agenda then comes the giant game of trying to spin the results to your side, it then ends up as a bunfight with both sides battering each other with their selected evidence until the mods exterminate the thread, much to every sane posters relief.
The Tiger about to under go an air burst test. The panel above the tank is to detonate the HE shell.
So the case for the accusation: there are four main reports widely available on the internet of a captured Panther, a Tiger, a King Tiger and the assessment of plate from a captured Panther.
Incidentally the British tested out the lower hull by stacking a box of No 75 anti-tank grenades, three non-boxed No 75's and a box of detonators, and buried it to the depth of two inches and then triggered the lot.
The results of the pile of explosives.

The most damning of the lot is the US metallurgical assessment and testing of German armour plate. Its given a high Brinell hardness of about 300, but lacking in a key material, and extremely brittle. Yet other reports from big cats (mostly tested by the British, with Soviet reports also suggesting the same) say that the plate is quite soft, surprisingly so, with a hardness of less than 250.
Most, if not all the sources say the same thing in their conclusions, that German plate is bad, but they do so for different reasons. Plus the Panther plate that was tested that lacked crucial ingredients is being cited as standard for all German armour, however this report comes from 1945.
All this might suggest that something else is going on.
The King Tiger before testing by the British.
Now in the defence we have Doyle backing up Thomas Jentz. In a book about the Tiger, in 1998, Jentz writes
"[...]there is no proof that substandard German armour plate was used during the last years of the war. All original documents confirm compliance with standard specifications throughout the war."
At first glance that looks like the Germans just produced some bad plate. But if that's the case, how can items from differing ends of the spectrum pass quality control? Or is there something else we might consider?
It might at this time be useful to point out that although I'm using phrases like "bad" or "poor" the plates tested by the British conformed roughly to what we called medium quality plate, known as IT80. So it's by no means terrible.
Some of No.1 Armoured car squadrons vehicles.
So what might be causing the differing results and the change in quality? Well exposure is a possible candidate. At least in the case of Tigers some of the tested ones were captured in North Africa, and there's an anecdote that I read about that might apply. A No.1 RAF Armoured Car Squadron was serving in the Middle East, in what is now Saudi Arabia. To overawe the locals a demonstration was put on for the Sheik, and a Rolls Royce armoured car was driven around at speed to display its prowess. The Sheik was informed of its bullet proof skin, and the officer invited the ruler to take a shot at the armoured car. The Sheik readily agreed and had his rifle brought forward. This turned out to be a colossal Jezail. This was duly fired and hit the car, much to the crew's surprise the bullet passed right through their armour! Luckily the car didn't display any signs of the penetrating hit and the British were able to bluff their way through and cover up the incident, they subsequently convinced the locals that taking on the might of the British Empire was a very bad idea. A very quick investigation showed that exposure to the temperatures and the sunlight had degraded the armour properties, to the point it wasn't actually effective. All the Rolls Royce armoured cars were quickly shipped back to the UK where they were re-armoured.
"I'll get you, you pesky Roller!"
At the other end of the spectrum you have the extreme cold of Russia, what effect does this have on armour one wonders. So without knowing the full history of all the German vehicles tested one can not say that they never encountered something such as this to effect their armour.

The other thing that struck me was the tests on Japanese plate. The thinnest Japanese plate was considered better than the equivalent British plate. This was I recall about 6mm. However as the plate increased in thickness the Japanese methods of treating the armour plate remained the same, and so the face hardening wasn't such a high percentage of the total depth of the plate and so the armour rapidly became worse than a British equivalent. This is what spawned my theory.
So maybe as armour thickness drastically increased then the German methods for treating the plate weren't able to keep up with the increase in thickness which caused the quality to drop. So while the treatments used maintained the standards required, it wasn't producing the same effect due to the increase in plate thickness. You’ll note that the drop in armour performance appears to link with the increase in armour to 100mm. Previously Panzers were manufactured with plate thickness of 50mm or lower. Mid war Panzer IV’s had 50mm plate with 30mm appliqué.
Of course as a theory it's just that. There's still several points of data required to confirm it. But it's just a thought.
Up armoured Panzer IV
Oh, and to clarify, and be blindingly clear: the myth of Krupp Steel is just that, the Germans didn't have a super special type of armour that was vastly in advance of everybody else, they had, and here's the surprise; armour plate just like everyone else. So when you see someone talking about a special German steel modifier (either for or against) ask yourself about their agenda. Because I suspect a lot more work will need to be done on this before either one side or the other has sufficient evidence to explain away all the holes in either argument.